Effects of deposition parameters and cobalt hexacyanocobaltate surface modification on magnetron-sputtered ZnIn₂S₄ thin film photoanodes
Abstract
For the first time, ZnIn₂S₄ (ZIS) thin films were successfully prepared by magnetron sputtering and systematically investigated as photoanodes for photoelectrochemical (PEC) water splitting. The PEC performance of the layers strongly depended on the deposition parameters. The highest photocurrent density of 2.77 mA cm⁻² at 1.62 V vs. RHE was achieved for films deposited at 200 °C for 90 min, whereas films deposited at 300 °C for 90 min exhibited improved stability. The optimized ZIS photoanode was subsequently modified with a cobalt hexacyanocobaltate (Cohcc) surface layer formed via electrooxidation of a Co layer in an electrolyte containing Co(CN)₆³⁻. This surface modification improved photoanode performance, particularly in terms of stability, likely due to enhanced oxygen evolution reaction (OER) kinetics at the electrode surface. Cohcc-modified photoanode generated almost 3 times higher photocurrent density after 100 s operation compared to unmodified photoanode. Electrochemical measurements performed under dark conditions further confirmed the role of Cohcc as cocatalyst toward OER. Overall, the results demonstrate that magnetron sputtering enables effective control over the properties of ZIS photoanodes through optimization of deposition parameters, while surface modification with cobalt hexacyanocobaltate represents a viable strategy for tuning interfacial kinetics and improving the functional performance of ZIS-based photoanodes.
Related
- Optical Emission Spectroscopy Applied to Plasma Magnetron Sputtering Metallic Deposition Onto Liquid at Low Pressure
- Agent-authored deposition recipes for X-ray multilayer mirrors: schema-bound LLM control of a magnetron sputtering system with reflectivity-verified outcomes
- Effect of independent parameters on nanoparticle sizes in magnetron-sputtering inert-gas condensation
- Adaptive Layered Deposition for Image Generation: A State-Dependent Framework for Progressive Construction, Selective Modification, and Variable-Depth Synthesis
- Catechol-based polydopamine modification of a dentin adhesive: effects on surface wettability, microhardness recovery, and mineral deposition
BibTeX
@article{roda2026effects,
title = {{Effects of deposition parameters and cobalt hexacyanocobaltate surface modification on magnetron-sputtered ZnIn₂S₄ thin film photoanodes}},
author = {D. Roda and K. Trzciński and M. Sawczak and A. Ilnicka and M. Szkoda and A. P. Nowak},
journal = {Scientific Reports},
year = {2026},
month = oct,
doi = {10.1038/s41598-026-74298-6},
url = {https://www.nature.com/articles/s41598-026-74298-6},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Effects of deposition parameters and cobalt hexacyanocobaltate surface modification on magnetron-sputtered ZnIn₂S₄ thin film photoanodes
AU - D. Roda
AU - K. Trzciński
AU - M. Sawczak
AU - A. Ilnicka
AU - M. Szkoda
AU - A. P. Nowak
PY - 2026
DA - 2026/10/01
JO - Scientific Reports
DO - 10.1038/s41598-026-74298-6
UR - https://www.nature.com/articles/s41598-026-74298-6
AB - For the first time, ZnIn₂S₄ (ZIS) thin films were successfully prepared by magnetron sputtering and systematically investigated as photoanodes for photoelectrochemical (PEC) water splitting. The PEC performance of the layers strongly depended on the deposition parameters. The highest photocurrent density of 2.77 mA cm⁻² at 1.62 V vs. RHE was achieved for films deposited at 200 °C for 90 min, whereas films deposited at 300 °C for 90 min exhibited improved stability. The optimized ZIS photoanode was subsequently modified with a cobalt hexacyanocobaltate (Cohcc) surface layer formed via electrooxidation of a Co layer in an electrolyte containing Co(CN)₆³⁻. This surface modification improved photoanode performance, particularly in terms of stability, likely due to enhanced oxygen evolution reaction (OER) kinetics at the electrode surface. Cohcc-modified photoanode generated almost 3 times higher photocurrent density after 100 s operation compared to unmodified photoanode. Electrochemical measurements performed under dark conditions further confirmed the role of Cohcc as cocatalyst toward OER. Overall, the results demonstrate that magnetron sputtering enables effective control over the properties of ZIS photoanodes through optimization of deposition parameters, while surface modification with cobalt hexacyanocobaltate represents a viable strategy for tuning interfacial kinetics and improving the functional performance of ZIS-based photoanodes.
SN - 2045-2322
ER -