Quantifying the Impact of Multiple Twin-Screw Extrusion Cycles on Discontinuous Carbon Fiber Composites
4 affiliations
- 1Bredesen Center for Interdisciplinary Research and Graduate Education, The University of Tennessee, Knoxville, TN 37996, USA
- 2Oak Ridge National Laboratory, Oak Ridge, TN 37831, USA
- 3Department of Chemistry, The University of Tennessee, Knoxville, TN 37996, USA
- 4Department of Mechanical and Aerospace Engineering, The University of Tennessee, Knoxville, TN 37996, USA
Abstract
To enable re-use, recycled fiber-filled thermoplastics may require intermediate processing, such as twin-screw compounding. These intermediate processes can introduce additional processing-induced degradation and performance variability. This study evaluated the recyclability of carbon-fiber-reinforced acrylonitrile butadiene styrene (CF-ABS) through ten consecutive pilot-scale extrusion cycles to determine the primary degradation mechanism as a function of lifetime and to quantify the impact on mechanical performance. Chemical analysis revealed that the ABS matrix remained chemically robust throughout repeated extrusion cycles, whereas optical microscopy showed that fiber breakage was significant. Fiber length exponentially decayed with repeated cycles, with the decay rate stabilizing between the 3rd and 5th cycle, resulting in a 62% reduction in weight-averaged fiber length from C0 to C10. The reduction in fiber length was found to govern both the rheological and mechanical behavior of the composite material. Viscosity and storage modulus decreased with decreasing fiber length while tan(δ) and elongation at break increased, shifting toward values characteristic of neat ABS and indicating a transition from fiber-dominant to matrix-dominant behavior. The tensile strength decreased 35% after the 10th cycle, and its decay behavior correlated with the decay rate of the measured fiber length. This correlation enabled the development of a simple analytical model to predict tensile strength, which predicted tensile strength more accurately than the Kelly–Tyson model (RMSE of 38 reduced to 3.5) and required fewer experimentally derived inputs. Overall, this study demonstrated that fiber breakage, rather than chemical degradation of the ABS matrix, dictates performance of recycled CF-ABS.
Related
- Synthesis of PEDOT particles and manufacturing of electrically-conductive PEO / PEDOT thermoplastic composites by twin-screw extrusion
- Empowering Polyamide/Glass fiber composites upcycling with energy sobriety formulations via reactive extrusion
- Increasing the Impact Strength of Grass Fiber Polypropylene Composites with Virgin and Recycled Polypropylene
- Low-Velocity Impact Response of Biaxial Glass-Fiber Fabric Composites: Influence of Fabric Layer Number Under Progressively Increasing Impact Energy
- Beyond ideal cavities: quantifying the impact of cavity dissipation on light-matter strong coupling
BibTeX
@article{walker2026quantifying,
title = {{Quantifying the Impact of Multiple Twin-Screw Extrusion Cycles on Discontinuous Carbon Fiber Composites}},
author = {Roo Walker and Matthew Korey and Amber M. Hubbard and Daniel Webb and Evan J. Holt and Ally Collier and Katie Copenhaver and S. Michael Kilbey and Soydan Ozcan and Chad Duty},
journal = {Polymers},
year = {2026},
month = oct,
doi = {10.3390/polym18212634},
url = {https://www.mdpi.com/2073-4360/18/21/2634},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Quantifying the Impact of Multiple Twin-Screw Extrusion Cycles on Discontinuous Carbon Fiber Composites
AU - Roo Walker
AU - Matthew Korey
AU - Amber M. Hubbard
AU - Daniel Webb
AU - Evan J. Holt
AU - Ally Collier
AU - Katie Copenhaver
AU - S. Michael Kilbey
AU - Soydan Ozcan
AU - Chad Duty
PY - 2026
DA - 2026/10/23
JO - Polymers
DO - 10.3390/polym18212634
UR - https://www.mdpi.com/2073-4360/18/21/2634
AB - To enable re-use, recycled fiber-filled thermoplastics may require intermediate processing, such as twin-screw compounding. These intermediate processes can introduce additional processing-induced degradation and performance variability. This study evaluated the recyclability of carbon-fiber-reinforced acrylonitrile butadiene styrene (CF-ABS) through ten consecutive pilot-scale extrusion cycles to determine the primary degradation mechanism as a function of lifetime and to quantify the impact on mechanical performance. Chemical analysis revealed that the ABS matrix remained chemically robust throughout repeated extrusion cycles, whereas optical microscopy showed that fiber breakage was significant. Fiber length exponentially decayed with repeated cycles, with the decay rate stabilizing between the 3rd and 5th cycle, resulting in a 62% reduction in weight-averaged fiber length from C0 to C10. The reduction in fiber length was found to govern both the rheological and mechanical behavior of the composite material. Viscosity and storage modulus decreased with decreasing fiber length while tan(δ) and elongation at break increased, shifting toward values characteristic of neat ABS and indicating a transition from fiber-dominant to matrix-dominant behavior. The tensile strength decreased 35% after the 10th cycle, and its decay behavior correlated with the decay rate of the measured fiber length. This correlation enabled the development of a simple analytical model to predict tensile strength, which predicted tensile strength more accurately than the Kelly–Tyson model (RMSE of 38 reduced to 3.5) and required fewer experimentally derived inputs. Overall, this study demonstrated that fiber breakage, rather than chemical degradation of the ABS matrix, dictates performance of recycled CF-ABS.
SN - 2073-4360
ER -