Experimental Investigation of Gypsum Composites Incorporating Polymeric Rubber Waste from the Vulcanization Industry
- 1Faculty of Civil Engineering, Mechanics and Petrochemistry, Warsaw University of Technology, Łukasiewicza 17, 09-400 Płock, Poland
Abstract
The aim of this study was to comprehensively evaluate the influence of rubber waste originating from the vulcanisation industry on the mechanical performance of gypsum composites. Three rubber fractions (0–0.6 mm, 0.3–1.5 mm and 1–4 mm) were incorporated at contents ranging from 0% to 50% of binder mass. Increasing rubber content resulted in a systematic reduction in composite density, decreasing from 1534 kg/m3 for the reference material to 1204 kg/m3, 1128 kg/m3 and 1031 kg/m3 at 50% addition for the three fractions, respectively. Flexural strength dropped from 0.296 MPa to 0.059 MPa (fine fraction) and 0.033 MPa (coarse fraction), while compressive strength decreased from 4.556 MPa to 1.542 MPa and 1.370 MPa at 25% rubber content. These results demonstrate that both particle size and quantitative share of rubber significantly affect the mechanical response of the composite. Generalised regression-based correlations were developed for flexural and compressive strength as a function of density and rubber content, providing practical descriptive models for the analysed range. The findings offer a quantitative basis for further research on the incorporation of rubber waste into gypsum-based materials and for assessing their potential use in non-structural applications.
Related
- Experimental investigation of microstructural and performance evolution in ultrasonic-assisted stir-cast AA8011–5 wt.% TiB₂ composites during multi-pass equal-channel angular pressing
- Quantum Computing for Polymeric Composites: Principles, Methods, Applications, and Future Perspectives
- Impeller Configuration and Agitation Speed Govern Lignin Dispersion and Resultant Properties of Natural Rubber Composites in Wet Mixing: A CFD Experimental Study
- Investigation on the Degradation Mechanisms and Mechanical Property Evolution of 3D-SiO2-Fiber-Reinforced Polyimide Composites After Thermal Aging
- Investigation of the influence of nutrient additives and the role of microstructure on the unconfined compression behaviour of mycelium composites
BibTeX
@article{pralat2026experimental,
title = {{Experimental Investigation of Gypsum Composites Incorporating Polymeric Rubber Waste from the Vulcanization Industry}},
author = {Karol Prałat and Justyna Ciemnicka and Michał Ciarkowski},
journal = {Polymers},
year = {2026},
month = oct,
doi = {10.3390/polym18212648},
url = {https://www.mdpi.com/2073-4360/18/21/2648},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Experimental Investigation of Gypsum Composites Incorporating Polymeric Rubber Waste from the Vulcanization Industry
AU - Karol Prałat
AU - Justyna Ciemnicka
AU - Michał Ciarkowski
PY - 2026
DA - 2026/10/26
JO - Polymers
DO - 10.3390/polym18212648
UR - https://www.mdpi.com/2073-4360/18/21/2648
AB - The aim of this study was to comprehensively evaluate the influence of rubber waste originating from the vulcanisation industry on the mechanical performance of gypsum composites. Three rubber fractions (0–0.6 mm, 0.3–1.5 mm and 1–4 mm) were incorporated at contents ranging from 0% to 50% of binder mass. Increasing rubber content resulted in a systematic reduction in composite density, decreasing from 1534 kg/m3 for the reference material to 1204 kg/m3, 1128 kg/m3 and 1031 kg/m3 at 50% addition for the three fractions, respectively. Flexural strength dropped from 0.296 MPa to 0.059 MPa (fine fraction) and 0.033 MPa (coarse fraction), while compressive strength decreased from 4.556 MPa to 1.542 MPa and 1.370 MPa at 25% rubber content. These results demonstrate that both particle size and quantitative share of rubber significantly affect the mechanical response of the composite. Generalised regression-based correlations were developed for flexural and compressive strength as a function of density and rubber content, providing practical descriptive models for the analysed range. The findings offer a quantitative basis for further research on the incorporation of rubber waste into gypsum-based materials and for assessing their potential use in non-structural applications.
SN - 2073-4360
ER -