Comparative Evaluation of Electrocoagulation for the Removal of Polyethylene and Polyvinyl Chloride Microplastics from Wastewater
- 1Department of Chemical Engineering, Dr. B. R. Ambedkar National Institute of Technology, Jalandhar 144008, Punjab, India
- 2Laboratory of Polymer and Dyes Chemistry and Technology, 54124 Thessaloniki, Greece
Abstract
The persistence of microplastics in aquatic environments has created a need for effective methods of their removal from wastewater. The physicochemical differences among the polymers can influence their behaviour during wastewater treatment and that poses a polymer-specific removal challenge. This study comparatively evaluates the removal behaviour of polyethylene (PE) and polyvinyl chloride (PVC) microplastics from synthetic wastewater using aluminium–copper electrodes and investigates the effect of electrolysis time on treatment performance. Batch experiments were conducted in a 500 mL reactor at 3 V and 0.012 A for 30, 60, 90 and 120 min. Removal and sludge capture were evaluated gravimetrically, while FESEM–EDS was employed to characterize the recovered microplastics and identify elemental deposition on their surfaces. FESEM-EDS analysis revealed the deposition of aluminium-containing coagulation products on the recovered PE and PVC surfaces following electrocoagulation. Maximum floc removal was obtained at 60 min, reaching 49.72% sludge removal for PE and 27.18% for PVC, with corresponding sludge capture efficiencies of 65.21% and 63.14%, respectively. Electrolysis treatment times below and above 60 min produced unstable flocs that in turn reduced the removal efficiency. The specific energy consumption at the studied condition was ~0.07 kWh m−3 for both polymers. Overall, the results demonstrate polymer-dependent removal behaviour and highlight the influence of electrolysis time on the treatment performance of PE and PVC microplastics under investigated conditions.
Related
- Hydrodynamic and electrochemical assessment of a compact continuous-flow electrocoagulation reactor for decentralized household wastewater treatment
- Synergistic Electrocoagulation–Electro-Fenton Coupling for Petroleum Refinery Wastewater Mineralization: Statistical Optimization and Cost Analysis
- Electrode performance in hybrid electrocoagulation and biochar adsorption systems for olive mill wastewater treatment
- Mechanistic insights into electrocoagulation-driven removal of polystyrene nanoplastics from urban treated wastewater
- Comparative evaluation of halloysite nanotubes and zirconium oxide nanoparticles for agricultural drainage wastewater treatment
BibTeX
@article{tiwari2026comparative,
title = {{Comparative Evaluation of Electrocoagulation for the Removal of Polyethylene and Polyvinyl Chloride Microplastics from Wastewater}},
author = {Bhavya Tiwari and Raj Kumar Arya and George D. Verros},
journal = {Polymers},
year = {2026},
month = oct,
doi = {10.3390/polym18202501},
url = {https://www.mdpi.com/2073-4360/18/20/2501},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Comparative Evaluation of Electrocoagulation for the Removal of Polyethylene and Polyvinyl Chloride Microplastics from Wastewater
AU - Bhavya Tiwari
AU - Raj Kumar Arya
AU - George D. Verros
PY - 2026
DA - 2026/10/01
JO - Polymers
DO - 10.3390/polym18202501
UR - https://www.mdpi.com/2073-4360/18/20/2501
AB - The persistence of microplastics in aquatic environments has created a need for effective methods of their removal from wastewater. The physicochemical differences among the polymers can influence their behaviour during wastewater treatment and that poses a polymer-specific removal challenge. This study comparatively evaluates the removal behaviour of polyethylene (PE) and polyvinyl chloride (PVC) microplastics from synthetic wastewater using aluminium–copper electrodes and investigates the effect of electrolysis time on treatment performance. Batch experiments were conducted in a 500 mL reactor at 3 V and 0.012 A for 30, 60, 90 and 120 min. Removal and sludge capture were evaluated gravimetrically, while FESEM–EDS was employed to characterize the recovered microplastics and identify elemental deposition on their surfaces. FESEM-EDS analysis revealed the deposition of aluminium-containing coagulation products on the recovered PE and PVC surfaces following electrocoagulation. Maximum floc removal was obtained at 60 min, reaching 49.72% sludge removal for PE and 27.18% for PVC, with corresponding sludge capture efficiencies of 65.21% and 63.14%, respectively. Electrolysis treatment times below and above 60 min produced unstable flocs that in turn reduced the removal efficiency. The specific energy consumption at the studied condition was ~0.07 kWh m−3 for both polymers. Overall, the results demonstrate polymer-dependent removal behaviour and highlight the influence of electrolysis time on the treatment performance of PE and PVC microplastics under investigated conditions.
SN - 2073-4360
ER -