Curing regime controlled performance of basalt-modified alkali activated slag: phase composition, porosity profile, microstructure and compressive strength
6 affiliations
- 1Department of Chemistry, Faculty of Science, Islamic University of Madinah Madinah 42351 Saudi Arabia
- 2Department of Chemistry, Faculty of Science, Ain Shams University Cairo Egypt
- 3Department of Chemistry, College of Science, King Faisal University Al-Ahsa 31982 Saudi Arabia
- 4Department of Physics, College of Science, King Faisal University Al-Ahsa 31982 Saudi Arabia
- 5Department of Biology, College of Science, Imam Mohammad Ibn Saud Islamic University (IMSIU) Riyadh 11623 Saudi Arabia
- 6Faculty of Engineering, Ain Shams University Cairo Egypt
Abstract
The transition from traditional cement to low-carbon alkali-activated materials is no longer an environmental obligation but a materials-design challenge requiring precise control of reaction kinetics. In this study, basalt-modified alkali-activated slag was cured under various conditions to demonstrate how mix design and curing regimes affect gel formation and strength development. Ground-granulated blast-furnace slag (GGBFS) was replaced with 5–20 wt% basalt (BT) and then activated with 6 wt% NaOH. The developed materials were cured under normal conditions (1–28 days), hydrothermal conditions (135–170 °C/5 h) and microwave conditions (450 W/5–15 min). Advanced microstructural analyses (XRD, FTIR, SEM/EDX and BET/BJH) elucidated the phase evolution, morphological features and porosity profile within the matrices. The results reveal that BT has a slight effect on the fresh properties (workability and setting time) of the alkali-activated slag. Despite diluting reactive calcium phases in GGBFS, the AAS-20BT (80% GGBFS + 20% BT) composite delivered robust, structural-grade compressive strengths: 49.5 MPa under normal curing, 56 MPa after 170 °C/5 h hydrothermal treatment, and a rapid 37 MPa after just 10 min at 450 W of microwave exposure. From the compressive-strength results and advanced analysis techniques, it can be concluded that the curing regime strongly controls the composition of the load-bearing capacity phases, microstructural development and pore refinement. Overall, hydrothermal curing provides the most favorable balance between reaction kinetics, zeolitic phase formation, hydrate morphology and microstructural development. Under normal conditions, BT particles act as fillers and nucleation seeds, while hydrothermal curing increases their reactivity, facilitating Si and Al dissolution and participation in geopolymeric products. Accordingly, the AAS-20BT can be considered a promising low-carbon binder that offers a highly scalable, eco-efficient pathway for next-generation construction materials.
Related
- Effect of Activator Modulus on the Performance, Reaction Products, and Microstructure of Biomass Power Plant Ash-Based Alkali-Activated Binders
- Effects of a Self-Developed Composite Modifier on the Compressive Strength, Shrinkage Behavior, and Microstructure of Cement-Stabilized Macadam
- Machine Learning-Driven Comparative Prediction of Compressive Strength in True Geopolymer and Hybrid Alkali-Activated Cement Systems
- Prediction model for compressive strength of alkali-activated multi-source solid-waste grouting materials based on generative adversarial networks and machine learning
- Compressive Performance of CFRP Ring-confined Circular LSCFST columns
BibTeX
@article{said2026curing,
title = {{Curing regime controlled performance of basalt-modified alkali activated slag: phase composition, porosity profile, microstructure and compressive strength}},
author = {Musa A. Said and M. Ramadan and Fatma. M. Helmy and Hany M. Abd El-Lateef and Mai M. Khalaf and Mohammed A. O. Basubaih and Saad Shaaban and Nagih M. Shaalan and Abdullah A. Saber and Alaa Mohsen},
journal = {RSC advances},
year = {2026},
month = oct,
doi = {10.1039/d6ra07623h},
url = {https://europepmc.org/article/PMC/PMC13663031},
note = {CC BY},
}
RIS
TY - JOUR
TI - Curing regime controlled performance of basalt-modified alkali activated slag: phase composition, porosity profile, microstructure and compressive strength
AU - Musa A. Said
AU - M. Ramadan
AU - Fatma. M. Helmy
AU - Hany M. Abd El-Lateef
AU - Mai M. Khalaf
AU - Mohammed A. O. Basubaih
AU - Saad Shaaban
AU - Nagih M. Shaalan
AU - Abdullah A. Saber
AU - Alaa Mohsen
PY - 2026
DA - 2026/10/14
JO - RSC advances
DO - 10.1039/d6ra07623h
UR - https://europepmc.org/article/PMC/PMC13663031
AB - The transition from traditional cement to low-carbon alkali-activated materials is no longer an environmental obligation but a materials-design challenge requiring precise control of reaction kinetics. In this study, basalt-modified alkali-activated slag was cured under various conditions to demonstrate how mix design and curing regimes affect gel formation and strength development. Ground-granulated blast-furnace slag (GGBFS) was replaced with 5–20 wt% basalt (BT) and then activated with 6 wt% NaOH. The developed materials were cured under normal conditions (1–28 days), hydrothermal conditions (135–170 °C/5 h) and microwave conditions (450 W/5–15 min). Advanced microstructural analyses (XRD, FTIR, SEM/EDX and BET/BJH) elucidated the phase evolution, morphological features and porosity profile within the matrices. The results reveal that BT has a slight effect on the fresh properties (workability and setting time) of the alkali-activated slag. Despite diluting reactive calcium phases in GGBFS, the AAS-20BT (80% GGBFS + 20% BT) composite delivered robust, structural-grade compressive strengths: 49.5 MPa under normal curing, 56 MPa after 170 °C/5 h hydrothermal treatment, and a rapid 37 MPa after just 10 min at 450 W of microwave exposure. From the compressive-strength results and advanced analysis techniques, it can be concluded that the curing regime strongly controls the composition of the load-bearing capacity phases, microstructural development and pore refinement. Overall, hydrothermal curing provides the most favorable balance between reaction kinetics, zeolitic phase formation, hydrate morphology and microstructural development. Under normal conditions, BT particles act as fillers and nucleation seeds, while hydrothermal curing increases their reactivity, facilitating Si and Al dissolution and participation in geopolymeric products. Accordingly, the AAS-20BT can be considered a promising low-carbon binder that offers a highly scalable, eco-efficient pathway for next-generation construction materials.
SN - 2046-2069
ER -