Hydrogen partial pressure as a key parameter in the reactive sputtering of photochromic YHO thin films
Abstract
Oxygen-containing yttrium hydride (YHO) thin films were synthesised by reactive magnetron sputtering over a wide range of hydrogen-to-argon gas flow ratios (H2/Ar) during yttrium hydride deposition, followed by post-oxidation in air. The deposition process was monitored in situ by plasma optical emission spectroscopy. X-ray diffraction reveals a strong dependence of crystallographic texture on the H2/Ar ratio: highly <100>-textured films formed at low H2/Ar ratios progressively evolve into more polycrystalline microstructures with slightly reduced crystallite size as the hydrogen content increases. The optical transmittance gradually decreases from approximately 85 % to 70 % as the H2/Ar ratio is raised to 0.6, followed by a sharp drop at higher hydrogen contents. The photochromic contrast of 705-845 nm thick YHO films, measured after 10 min of illumination with a solar simulator, decreases from 14 % to 7 % as the H2/Ar ratio increases from 0.08 to 0.45. Thinner films (365-505 nm) exhibit a similar but less pronounced trend. Bleaching kinetics, analysed using a double-exponential model, indicate faster recovery, with effective bleaching time constants of approximately 1-15 min for films deposited at H2/Ar < 0.25. X-ray photoelectron spectroscopy reveals higher oxygen incorporation in films deposited at lower H2/Ar ratios, deviating from the commonly reported correlation between oxygen content and photochromic response in YHO. These results demonstrate that low hydrogen partial pressure during reactive sputtering is advantageous for achieving higher optical transparency, enhanced photochromic contrast, and faster bleaching kinetics in YHO thin films.
Versions
Related
- Multi-techniques characterisation of anti-reflective Ta2O5 and TaOxNy thin films deposited by reactive sputtering: coupling X-ray photoelectron spectroscopy, scanning/transmission electron microscopy and ion beam analysis
- Optical Emission Spectroscopy Applied to Plasma Magnetron Sputtering Metallic Deposition Onto Liquid at Low Pressure
- Grid-based quantum circuit simulation of the hydrogen atom: Coulomb singularity regularization and parameter-selection guidelines
- Pressure Evolution of the Superconducting Order Parameter of Kagome Superconductor CsV3Sb5
- Libron-phonon coupling and hydrogen-bond dynamics in the vacancy-ordered perovskite (NH4)2SnCl6: a temperature- and pressure-dependent Raman study
BibTeX
@misc{strods2026hydrogen,
title = {{Hydrogen partial pressure as a key parameter in the reactive sputtering of photochromic YHO thin films}},
author = {E. Strods and M. Zubkins and E. Letko and V. Vibornijs and A. Sarakovskis and J. Purans},
howpublished = {arXiv},
year = {2026},
month = oct,
doi = {10.48550/arxiv.2610.18068},
eprint = {2610.18068},
archivePrefix = {arXiv},
url = {https://arxiv.org/abs/2610.18068},
note = {CC BY-NC-ND 4.0},
}
RIS
TY - UNPB
TI - Hydrogen partial pressure as a key parameter in the reactive sputtering of photochromic YHO thin films
AU - E. Strods
AU - M. Zubkins
AU - E. Letko
AU - V. Vibornijs
AU - A. Sarakovskis
AU - J. Purans
PY - 2026
DA - 2026/10/14
PB - arXiv
DO - 10.48550/arxiv.2610.18068
UR - https://arxiv.org/abs/2610.18068
AB - Oxygen-containing yttrium hydride (YHO) thin films were synthesised by reactive magnetron sputtering over a wide range of hydrogen-to-argon gas flow ratios (H2/Ar) during yttrium hydride deposition, followed by post-oxidation in air. The deposition process was monitored in situ by plasma optical emission spectroscopy. X-ray diffraction reveals a strong dependence of crystallographic texture on the H2/Ar ratio: highly <100>-textured films formed at low H2/Ar ratios progressively evolve into more polycrystalline microstructures with slightly reduced crystallite size as the hydrogen content increases. The optical transmittance gradually decreases from approximately 85 % to 70 % as the H2/Ar ratio is raised to 0.6, followed by a sharp drop at higher hydrogen contents. The photochromic contrast of 705-845 nm thick YHO films, measured after 10 min of illumination with a solar simulator, decreases from 14 % to 7 % as the H2/Ar ratio increases from 0.08 to 0.45. Thinner films (365-505 nm) exhibit a similar but less pronounced trend. Bleaching kinetics, analysed using a double-exponential model, indicate faster recovery, with effective bleaching time constants of approximately 1-15 min for films deposited at H2/Ar < 0.25. X-ray photoelectron spectroscopy reveals higher oxygen incorporation in films deposited at lower H2/Ar ratios, deviating from the commonly reported correlation between oxygen content and photochromic response in YHO. These results demonstrate that low hydrogen partial pressure during reactive sputtering is advantageous for achieving higher optical transparency, enhanced photochromic contrast, and faster bleaching kinetics in YHO thin films.
ER -