Effects of immediate and delayed light curing and polishing on the mechanical properties of resin-modified glass ionomer cements
Abstract
Background: Resin-modified glass ionomer cements (RMGICs) are among the most widely used restorative materials in dentistry. Identifying the factors that influence their mechanical properties is essential for optimizing their clinical performance. However, the combined effects of immediate and delayed light curing and polishing on the mechanical properties and surface roughness of RMGICs have not been thoroughly investigated. Materials and Methods: This was an in vitro experimental study. Twenty-four disc-shaped specimens were prepared from two RMGICs: GC Fuji II LC and SDI RIVA Light Cure. Half of the specimens were light-cured immediately after placement, whereas the remaining specimens were light-cured after a 4-min delay. Each light-curing group was further divided into two subgroups according to the polishing protocol: immediate polishing and delayed polishing (after 24 h). Nano-indentation testing was performed to determine hardness, elastic modulus, and creep. Surface roughness was evaluated using atomic force microscopy (AFM). Data were analyzed using the independent-samples t-test, one-way analysis of variance (ANOVA), Tukey’s post hoc test, and three-way ANOVA. The level of statistical significance was set at P < 0.05. Results: Immediate light curing resulted in significantly higher hardness and elastic modulus than delayed light curing, whereas no significant difference was observed in creeP values. Immediate polishing produced a significantly higher elastic modulus than delayed polishing, while hardness and creep were not significantly affected by polishing time. GC Fuji II LC exhibited significantly higher hardness (0.96 ± 0.41 GPa) and lower creep (9.52% ±3.05%) than SDI RIVA Light Cure (0.74 ± 0.27 GPa and 13.73% ±3.33%, respectively). Surface roughness was not significantly influenced by the material type, light-curing protocol, or polishing protocol. Conclusion: Immediate light curing significantly improved the mechanical properties of the tested RMGICs, whereas immediate polishing did not adversely affect their performance. Therefore, performing both procedures immediately may reduce clinical chairside time without compromising the materials’ mechanical properties.
Related
- Study on the mechanical properties and consolidation mechanism of dispersive soil modified with nano-clay
- Mechanical properties of diatomite modified concrete with different moisture contents after high temperature treatment
- Management of Severe Dentoalveolar Trauma Following a Motorcycle Accident With Immediate Ridge Preservation and Delayed Implant Rehabilitation: A Case Report
- Phenotype Switching From Delayed Cutaneous Reactions to Immediate Anaphylaxis Upon Rechallenge With Paclitaxel.
- Comparative Analysis of Buccal and Lingual Bone Thicknesses Following Immediate and Delayed Loading of Posterior Mandibular Implants
BibTeX
@article{ghasemi2026effects,
title = {{Effects of immediate and delayed light curing and polishing on the mechanical properties of resin-modified glass ionomer cements}},
author = {Maede Ghasemi and Leyla Ghorbani and Reza Abedinzadeh},
journal = {Dental Research Journal},
year = {2026},
month = sep,
doi = {10.4103/drj.drj_60_26},
url = {https://doi.org/10.4103/drj.drj_60_26},
note = {CC BY-NC-SA},
}
RIS
TY - JOUR
TI - Effects of immediate and delayed light curing and polishing on the mechanical properties of resin-modified glass ionomer cements
AU - Maede Ghasemi
AU - Leyla Ghorbani
AU - Reza Abedinzadeh
PY - 2026
DA - 2026/09/01
JO - Dental Research Journal
DO - 10.4103/drj.drj_60_26
UR - https://doi.org/10.4103/drj.drj_60_26
AB - Background: Resin-modified glass ionomer cements (RMGICs) are among the most widely used restorative materials in dentistry. Identifying the factors that influence their mechanical properties is essential for optimizing their clinical performance. However, the combined effects of immediate and delayed light curing and polishing on the mechanical properties and surface roughness of RMGICs have not been thoroughly investigated. Materials and Methods: This was an in vitro experimental study. Twenty-four disc-shaped specimens were prepared from two RMGICs: GC Fuji II LC and SDI RIVA Light Cure. Half of the specimens were light-cured immediately after placement, whereas the remaining specimens were light-cured after a 4-min delay. Each light-curing group was further divided into two subgroups according to the polishing protocol: immediate polishing and delayed polishing (after 24 h). Nano-indentation testing was performed to determine hardness, elastic modulus, and creep. Surface roughness was evaluated using atomic force microscopy (AFM). Data were analyzed using the independent-samples t-test, one-way analysis of variance (ANOVA), Tukey’s post hoc test, and three-way ANOVA. The level of statistical significance was set at P < 0.05. Results: Immediate light curing resulted in significantly higher hardness and elastic modulus than delayed light curing, whereas no significant difference was observed in creeP values. Immediate polishing produced a significantly higher elastic modulus than delayed polishing, while hardness and creep were not significantly affected by polishing time. GC Fuji II LC exhibited significantly higher hardness (0.96 ± 0.41 GPa) and lower creep (9.52% ±3.05%) than SDI RIVA Light Cure (0.74 ± 0.27 GPa and 13.73% ±3.33%, respectively). Surface roughness was not significantly influenced by the material type, light-curing protocol, or polishing protocol. Conclusion: Immediate light curing significantly improved the mechanical properties of the tested RMGICs, whereas immediate polishing did not adversely affect their performance. Therefore, performing both procedures immediately may reduce clinical chairside time without compromising the materials’ mechanical properties.
SN - 1735-3327
SN - 2008-0255
ER -