Bottom-up assembly of graphene-decorated d-MXene nanoarchitecture for enhanced antibacterial activity against Escherichia coli and Bacillus cereus
- 1Ionic Liquid and Nano Materials Laboratory, Department of Physics, Faculty of Engineering and Technology, V. B. S. Purvanchal University, Jaunpur, India
- 2Department of Biotechnology, V. B. S. Purvanchal University, Jaunpur, India
Abstract
A bottom-up ultrasonication-assisted strategy was employed for the assembly of graphene-decorated d-MXene nanoarchitectures, and their antibacterial activity against Escherichia coli and Bacillus cereus was systematically investigated. The formation of the nanoarchitecture was confirmed through complementary morphological, structural, spectroscopic, and surface charge analyses. Scanning electron microscopy, elemental mapping, and high-resolution transmission electron microscopy observations revealed the uniform decoration of graphene nanosheets over layered d-MXene sheets, resulting in a structurally open architecture with suppressed nanosheet restacking. Powder X-ray diffraction (PXRD) analysis exhibited peak broadening, intensity variation, and modification of the low-angle (002) reflection, while comparative PXRD analysis with a composition-matched physical mixture further demonstrated disruption of the d-MXene stacking order following ultrasonication-assisted assembly. Raman spectroscopy exhibited the coexistence of graphene D (1339 cm−1) and G (1581 cm−1) bands together with the characteristic d-MXene vibrational mode at 153 cm−1 confirming preservation of defect-associated graphene domains within the assembled nanoarchitecture. Comparative Raman analysis further revealed systematic shifts in the characteristic graphene and d-MXene bands and a decrease in the ID/IG ratio from 1.83 for the physical mixture to 1.27 for the nanoarchitecture, supporting intimate interfacial organization. X-ray photoelectron spectroscopy analysis revealed the coexistence of sp2 C=C (284.1 eV), sp3 C–C (284.7 eV), Ti–C (282.5 eV), and Ti–O (530.5 eV) bonding states, suggesting effective interfacial coupling and defect enriched surface regions after nanoarchitecture formation. Zeta potential analysis demonstrated enhanced colloidal stability of the graphene-decorated d-MXene nanoarchitecture with a highly negative surface charge value of −84.04 mV compared to graphene nanosheets (−54.7 mV) and d-MXene (−44.98 mV), indicating enhanced electrostatic stabilization and improved dispersion stability after nanoarchitecture formation. Dynamic light scattering analysis additionally revealed a reduction in average hydrodynamic size from 1658 nm for pristine d-MXene to 1211 nm after graphene incorporation, confirming suppression of nanosheets agglomeration within the assembled nanoarchitecture. The antibacterial activity was evaluated using colony-forming unit (CFU) and OD600 growth assays. The graphene-decorated d-MXene nanoarchitectures exhibited concentration-dependent antibacterial activity, reducing bacterial viability from 4.00 × 105/4.20 × 105 to 1.80 × 104/2.10 × 104 CFU/mL after 24 h at 500 µg/mL. Similarly, bacterial growth was significantly suppressed, with OD600 decreasing from 2.54/2.80 for untreated E. coli/B. cereus to 0.54/0.59 after treatment. Compared to a recent report (Ag/Ti3CNTx), the present system shows ≈39% relative reduction in E. coli viability without requiring silver doping. The enhanced activity is attributed to the cooperative contribution of improved nanosheet accessibility, membrane contact probability, exposed active interfacial domains, and a possible additional ROS-mediated pathway.
Related
- Magnetic Correlations in Co/CoO Core/Shell Nanoparticles Decorated on Graphene: Insights from a Modified 2D Law of Approaching Magnetic Saturation
- Development of Fe3O4@SiO2 Magnetic Nanobeads Decorated with Graphene Oxide for Improved DNA Separation
- Charge-state-controlled spin polarization and quantum transport in vanadium-decorated 7-armchair graphene nanoribbons.
- Surface Modification of ZnO Nanoparticles with L-Serine and Preliminary Antibacterial Properties Against Escherichia coli
- Multifunctional Antibacterial Nanocomposites Based on Graphene Oxide, Graphitic Carbon Nitride, and Cobalt Ferrite Functionalized with an Antimicrobial Polymer Blend and Silver Nanoparticles for Biomedical and Environmental Applications
BibTeX
@article{kumar2026bottomup,
title = {{Bottom-up assembly of graphene-decorated d-MXene nanoarchitecture for enhanced antibacterial activity against Escherichia coli and Bacillus cereus}},
author = {Avdhesh Kumar and Ankit Singh and Ishani Bharti and Chandra Bhushan and Ram Naraian and Manish Pratap Singh},
journal = {Beilstein Journal of Nanotechnology},
year = {2026},
month = oct,
doi = {10.3762/bjnano.17.100},
url = {https://doi.org/10.3762/bjnano.17.100},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Bottom-up assembly of graphene-decorated d-MXene nanoarchitecture for enhanced antibacterial activity against Escherichia coli and Bacillus cereus
AU - Avdhesh Kumar
AU - Ankit Singh
AU - Ishani Bharti
AU - Chandra Bhushan
AU - Ram Naraian
AU - Manish Pratap Singh
PY - 2026
DA - 2026/10/22
JO - Beilstein Journal of Nanotechnology
DO - 10.3762/bjnano.17.100
UR - https://doi.org/10.3762/bjnano.17.100
AB - A bottom-up ultrasonication-assisted strategy was employed for the assembly of graphene-decorated d-MXene nanoarchitectures, and their antibacterial activity against Escherichia coli and Bacillus cereus was systematically investigated. The formation of the nanoarchitecture was confirmed through complementary morphological, structural, spectroscopic, and surface charge analyses. Scanning electron microscopy, elemental mapping, and high-resolution transmission electron microscopy observations revealed the uniform decoration of graphene nanosheets over layered d-MXene sheets, resulting in a structurally open architecture with suppressed nanosheet restacking. Powder X-ray diffraction (PXRD) analysis exhibited peak broadening, intensity variation, and modification of the low-angle (002) reflection, while comparative PXRD analysis with a composition-matched physical mixture further demonstrated disruption of the d-MXene stacking order following ultrasonication-assisted assembly. Raman spectroscopy exhibited the coexistence of graphene D (1339 cm−1) and G (1581 cm−1) bands together with the characteristic d-MXene vibrational mode at 153 cm−1 confirming preservation of defect-associated graphene domains within the assembled nanoarchitecture. Comparative Raman analysis further revealed systematic shifts in the characteristic graphene and d-MXene bands and a decrease in the ID/IG ratio from 1.83 for the physical mixture to 1.27 for the nanoarchitecture, supporting intimate interfacial organization. X-ray photoelectron spectroscopy analysis revealed the coexistence of sp2 C=C (284.1 eV), sp3 C–C (284.7 eV), Ti–C (282.5 eV), and Ti–O (530.5 eV) bonding states, suggesting effective interfacial coupling and defect enriched surface regions after nanoarchitecture formation. Zeta potential analysis demonstrated enhanced colloidal stability of the graphene-decorated d-MXene nanoarchitecture with a highly negative surface charge value of −84.04 mV compared to graphene nanosheets (−54.7 mV) and d-MXene (−44.98 mV), indicating enhanced electrostatic stabilization and improved dispersion stability after nanoarchitecture formation. Dynamic light scattering analysis additionally revealed a reduction in average hydrodynamic size from 1658 nm for pristine d-MXene to 1211 nm after graphene incorporation, confirming suppression of nanosheets agglomeration within the assembled nanoarchitecture. The antibacterial activity was evaluated using colony-forming unit (CFU) and OD600 growth assays. The graphene-decorated d-MXene nanoarchitectures exhibited concentration-dependent antibacterial activity, reducing bacterial viability from 4.00 × 105/4.20 × 105 to 1.80 × 104/2.10 × 104 CFU/mL after 24 h at 500 µg/mL. Similarly, bacterial growth was significantly suppressed, with OD600 decreasing from 2.54/2.80 for untreated E. coli/B. cereus to 0.54/0.59 after treatment. Compared to a recent report (Ag/Ti3CNTx), the present system shows ≈39% relative reduction in E. coli viability without requiring silver doping. The enhanced activity is attributed to the cooperative contribution of improved nanosheet accessibility, membrane contact probability, exposed active interfacial domains, and a possible additional ROS-mediated pathway.
SN - 2190-4286
ER -