Non-Destructive Mechanical Characterization of 4680 Cylindrical Lithium-Ion Cells for Cell-to-X Integration
- 1Department Battery Engineering & Safety, Production Engineering of E-Mobility Components (PEM), RWTH Aachen University, 52056 Aachen, Germany
- 2RheinNetz GmbH, 50823 Cologne, Germany
Abstract
Electric vehicles offer a sustainable alternative to combustion engines but still face range and safety limitations. Integrating battery cells as structural elements (Cell-to-X, CTX) is a promising route to address both, but requires cells that reliably withstand everyday mechanical loads. This study presents a non-destructive mechanical characterization of commercial 4680-format cylindrical lithium-ion cells (Supplier 1), combining quasi-static compression tests (hemispherical and cylindrical indenters) across state of charge (SOC) and indentation depth, cyclic aging over up to 150 cycles, and post-mortem computed tomography (CT) analysis. Deformation remained predominantly reversible up to indentation depths of 0.5 mm for the hemispherical and 1.8 mm for the cylindrical indenter, and peak forces of up to 9.16 kN were sustained without functional or electrical failure, although localized plastic casing deformation was observed in individual cells at the highest tested depths. For the cylindrical indenter, peak force increased consistently with SOC and indentation depth, consistent with prior literature, while temperature and voltage remained stable throughout loading, with no immediate evidence of an internal short circuit. For the cells with a sufficiently complete cycling record, capacity loss over the valid cycles amounted to 1.8–2.9% per 100 cycles for the mechanically loaded cells, compared with 2.0% for an unstressed reference cell. Post-mortem CT imaging confirmed deformation remained confined to the outer casing and outermost jelly-roll layers without affecting internal structure or performance. These results provide preliminary evidence that the tested cells can tolerate structurally relevant mechanical loads without loss of function, supporting further development of CTX architectures.
Related
- Failure Characteristics of Cylindrical Cells (18650 and 26700) Across Sodium-Ion, Lithium Nickel Manganese Cobalt Oxide (NMC), Lithium Iron Phosphate (LFP) and Lithium Titanate (LTO) Chemistries
- Passive Thermal Management of Cylindrical Lithium-Ion Cells Using Additively Manufactured Polymer Housings
- Structure–Performance Interplay and Mechanical Degradation Modes in Lithium Cobalt Oxide Cathodes: Implications for Flexible Lithium-Ion Battery Design
- State-of-Health Diagnostics in Lithium-Ion Batteries: A Methodological Framework for Scalable Mechanical Ageing Assessments
- Why Electrochemical–Thermal–Mechanical Understanding is Needed to Explain Knees in Lithium-Ion Batteries Degradation
BibTeX
@article{ghandily2026nondestructive,
title = {{Non-Destructive Mechanical Characterization of 4680 Cylindrical Lithium-Ion Cells for Cell-to-X Integration}},
author = {Nima Ghandily and Rizwan Javed and Niklas Kisseler and Heiner Heimes and Achim Kampker},
journal = {Batteries},
year = {2026},
month = oct,
doi = {10.3390/batteries12100429},
url = {https://www.mdpi.com/2313-0105/12/10/429},
note = {CC BY 4.0},
}
RIS
TY - JOUR
TI - Non-Destructive Mechanical Characterization of 4680 Cylindrical Lithium-Ion Cells for Cell-to-X Integration
AU - Nima Ghandily
AU - Rizwan Javed
AU - Niklas Kisseler
AU - Heiner Heimes
AU - Achim Kampker
PY - 2026
DA - 2026/10/15
JO - Batteries
DO - 10.3390/batteries12100429
UR - https://www.mdpi.com/2313-0105/12/10/429
AB - Electric vehicles offer a sustainable alternative to combustion engines but still face range and safety limitations. Integrating battery cells as structural elements (Cell-to-X, CTX) is a promising route to address both, but requires cells that reliably withstand everyday mechanical loads. This study presents a non-destructive mechanical characterization of commercial 4680-format cylindrical lithium-ion cells (Supplier 1), combining quasi-static compression tests (hemispherical and cylindrical indenters) across state of charge (SOC) and indentation depth, cyclic aging over up to 150 cycles, and post-mortem computed tomography (CT) analysis. Deformation remained predominantly reversible up to indentation depths of 0.5 mm for the hemispherical and 1.8 mm for the cylindrical indenter, and peak forces of up to 9.16 kN were sustained without functional or electrical failure, although localized plastic casing deformation was observed in individual cells at the highest tested depths. For the cylindrical indenter, peak force increased consistently with SOC and indentation depth, consistent with prior literature, while temperature and voltage remained stable throughout loading, with no immediate evidence of an internal short circuit. For the cells with a sufficiently complete cycling record, capacity loss over the valid cycles amounted to 1.8–2.9% per 100 cycles for the mechanically loaded cells, compared with 2.0% for an unstressed reference cell. Post-mortem CT imaging confirmed deformation remained confined to the outer casing and outermost jelly-roll layers without affecting internal structure or performance. These results provide preliminary evidence that the tested cells can tolerate structurally relevant mechanical loads without loss of function, supporting further development of CTX architectures.
SN - 2313-0105
ER -