Fabrication and Characterization of 3D-Printed Polylactide Composite Scaffolds with Modified Graphene
5 affiliations
- 1Thammasat University , , ,
- 2Université Claude Bernard Lyon 1 , , ,
- 3Chulalongkorn University , , ,
- 4Thailand Science Park , , ,
- 5Institute of Science Tokyo , , 2-12-1, O̅okayama , Meguro-Ku, ,
Abstract
In this study, we introduce novel multifunctional biomaterial inks for extrusion-based 3D bioprinting to create scaffolds for potential tissue engineering. This study focuses on developing composite materials by incorporating alkyl ketene dimer (AKD)-modified graphene nanoplatelets (GP) into polylactide (PLA) using a solvent casting technique. GP was synthesized via electrolytic exfoliation in an aqueous poly(sodium 4-styrenesulfonate) solution and subsequently modified with AKD by ball milling to enhance dispersion and PLA compatibility. Physical and chemical characterization confirmed the successful synthesis and structural properties of the AKD-modified GP. PLA-GPD20 films containing 20 wt % AKD-modified GP exhibited significantly improved elongation at break and maintained tensile strength comparable to neat PLA. All biomaterial composite films exhibited high stiffness, as evidenced by glass transition temperatures above room temperature, and electrical conductivity in the semiconductor range. The results highlight the significant positive impact of AKD on the physical and electrical properties, as well as the printability, of the composites. The printability performance potential was evaluated using 10 wt % PLA-GPD20 biomaterial inks to generate scaffolds with different patterns. The mechanical testing of the printed scaffolds revealed that the tensile strength and modulus increased with the incorporation of GPD20. The printing orientation is an effective parameter for tuning the balance between stiffness and ductility; scaffolds printed at 90° exhibited higher Young’s modulus but lower elongation at yield and tensile strength than those printed at 45°. Furthermore, incorporating AKD into GP/PLA composites improved hydrophobicity. The results suggest that AKD-modified graphene composites hold substantial promise for the development of advanced multifunctional materials for tissue engineering applications.
Related
- Fabrication and Characterization of Chitosan-Integrated Polyvinyl Alcohol–Polycaprolactone/Tea Tree Oil Nanofibrous Scaffolds via Dual-Nozzle Electrospinning for Wound Dressing Applications
- Biomimetic Fabrication and Osteogenic Efficacy Evaluation of Tilapia-Derived Collagen-Based Artificial Bone Scaffolds
- Fabrication and Optimization of 3D-Printed TiO2/g-C3N4 Scaffolds for Degradation of Organic Dye and Pharmaceutical Pollutant
- Fabrication of Electrospun PAN–CNT–CNC Composite Nanofiber Films for Hydrovoltaic Energy Harvesting
- In situ multiscale XCT degradation study of PEO-modified WE43 scaffolds: Correlating microstructure with hydrogen evolution
BibTeX
@article{khimlek2026fabrication,
title = {{Fabrication and Characterization of 3D-Printed Polylactide Composite Scaffolds with Modified Graphene}},
author = {Worathep Khimlek and Jirawan Jindakeaw and Vitsarut Primpray and Chanpen Karuwan and Teruoki Tago and Paiboon Sreearunothai and Chariya Kaewsaneha and Adisorn Tuantranont and Pakorn Opaprakasit},
journal = {ACS Omega},
year = {2026},
month = oct,
doi = {10.1021/acsomega.6c04916},
url = {https://pubs.acs.org/acsodf/article/doi/10.1021/acsomega.6c04916/5459456/Fabrication-and-Characterization-of-3D-Printed},
note = {CC BY-NC-ND 4.0},
}
RIS
TY - JOUR
TI - Fabrication and Characterization of 3D-Printed Polylactide Composite Scaffolds with Modified Graphene
AU - Worathep Khimlek
AU - Jirawan Jindakeaw
AU - Vitsarut Primpray
AU - Chanpen Karuwan
AU - Teruoki Tago
AU - Paiboon Sreearunothai
AU - Chariya Kaewsaneha
AU - Adisorn Tuantranont
AU - Pakorn Opaprakasit
PY - 2026
DA - 2026/10/27
JO - ACS Omega
DO - 10.1021/acsomega.6c04916
UR - https://pubs.acs.org/acsodf/article/doi/10.1021/acsomega.6c04916/5459456/Fabrication-and-Characterization-of-3D-Printed
AB - In this study, we introduce novel multifunctional biomaterial inks for extrusion-based 3D bioprinting to create scaffolds for potential tissue engineering. This study focuses on developing composite materials by incorporating alkyl ketene dimer (AKD)-modified graphene nanoplatelets (GP) into polylactide (PLA) using a solvent casting technique. GP was synthesized via electrolytic exfoliation in an aqueous poly(sodium 4-styrenesulfonate) solution and subsequently modified with AKD by ball milling to enhance dispersion and PLA compatibility. Physical and chemical characterization confirmed the successful synthesis and structural properties of the AKD-modified GP. PLA-GPD20 films containing 20 wt % AKD-modified GP exhibited significantly improved elongation at break and maintained tensile strength comparable to neat PLA. All biomaterial composite films exhibited high stiffness, as evidenced by glass transition temperatures above room temperature, and electrical conductivity in the semiconductor range. The results highlight the significant positive impact of AKD on the physical and electrical properties, as well as the printability, of the composites. The printability performance potential was evaluated using 10 wt % PLA-GPD20 biomaterial inks to generate scaffolds with different patterns. The mechanical testing of the printed scaffolds revealed that the tensile strength and modulus increased with the incorporation of GPD20. The printing orientation is an effective parameter for tuning the balance between stiffness and ductility; scaffolds printed at 90° exhibited higher Young’s modulus but lower elongation at yield and tensile strength than those printed at 45°. Furthermore, incorporating AKD into GP/PLA composites improved hydrophobicity. The results suggest that AKD-modified graphene composites hold substantial promise for the development of advanced multifunctional materials for tissue engineering applications.
SN - 2470-1343
ER -